【摘要】Sialon ceramics were prepared by the nitridation of Si,Al and Al2O3 powders with the transition metals(Fe Co,Ni)catalysts.The phase composition,microstructure and mechanical properties of specimens were studied Compared with the catalyst-free specimen,the addition of Fe,Co and Ni greatly promoted the nitridation process of Sialon ceramics and improved the weight gain rate and mechanical properties of specimens.With the increased content of catalysts,the apparent porosity of the products decreased first and then increased,contrary to flexural strength and compressive strength.The specimen with 2.5 wt%Fe had the highest flexural strength 145.8 MPa and it exhibited the highest compressive strength of 594.6 MPa when Co content was 2.5 wt%,whereas they were 71.9 and 78.7 MPa,respectively,when without catalyst.
【关键词】
《建筑知识》 2015-05-12
《中国医疗管理科学》 2015-05-12
《中国医疗管理科学》 2015-05-12
《中国医疗管理科学》 2015-05-12
《中外医疗》 2015-07-06
《现代制造技术与装备》 2015-06-25
《重庆电子工程职业学院学报》 2015-07-02
《重庆高教研究》 2015-06-30
Copyright © 2013-2016 ZJHJ Corporation,All Rights Reserved
发表评论
登录后发表评论 (已发布 0条)点亮你的头像 秀出你的观点